Preparation and characterization of a solid polymer electrolyte PEO‐ENR50 (80/20)‐LiCF3SO3 Academic Article uri icon

abstract

  • AbstractThe preparation and characterization of a polymer electrolyte films containing 80 wt % of poly (ethylene oxide) (PEO) and 20 wt % epoxidized natural rubber (ENR50) complexed with LiCF3SO3 has been reported. The ac impedance data showed good conducting properties of the solid polymer electrolyte (SPE) films. The greatest room temperature ionic conductivity of 7.5 × 10−5 S cm−1 was obtained at 25 wt % of LiCF3SO3 salt. This result has been supported by differential scanning calorimeter and X‐ray diffraction analysis. Analysis differential scanning calorimetry showed the relative percentage of crystallinity and Tm of PEO decreased with the increasing wt % of LiCF3SO3. Analysis with X‐ray diffraction suggested that the semicrystalline nature of PEO turned to amorphous due to the presence of LiCF3SO3. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009

publication date

  • 2009

number of pages

  • 4

start page

  • 855

end page

  • 859

volume

  • 113

issue

  • 2